| 牌 號(hào) | 狀 態(tài) | 直 徑/mm | 抗拉強(qiáng)度σb/MPa | 伸 長(zhǎng) 率（%） | 布氏硬度（HBS） | |
| δ10 | δ5 | |||||
| ≥ | ||||||
| T2，T3 | R | 30~120 | 186 | 30 | 40 | - |
| TU1，TU2，TP2 | R | 16~120 | - | - | - | - |
| H96 | R | 16~80 | 196 | 30 | - | - |
| H96 | R | >80~120 | - | - | - | - |
| H80 | R | 16~120 | - | - | - | - |
| H68 | R | 16~80 | 295 | 40 | 45 | - |
| H68 | R | >80~120 | - | - | - | - |
| H62 | R | 10~160 | 295 | 30 | 35 | - |
| H59 | R | 16~120 | - | - | - | - |
| HPb59-1 | R | 10~160 | 365 | 18 | 21 | - |
| HSn52-1 | R | 10~120 | 265 | 20 | 22 | - |
| HSn52-1 | R | >120~160 | - | - | - | - |
| HSn70-1 | R | 10~75 | 245 | 40 | - | - |
| HSn70-1 | R | >75~160 | - | - | - | - |
| HMn58-2 | R | 10~120 | 395 | 25 | 29 | - |
| HMn58-2 | R | >120~160 | - | - | - | - |
| HMn55-3-1 | R | 10~75 | 490 | 15 | - | - |
| HMn55-3-1 | R | >75~160 | - | - | - | - |
| HMn57-3-1 | R | 10~70 | 490 | 15 | 16 | - |
| HMn57-3-1 | R | >70~160 | - | - | - | - |
| HFe58-1-1 | R | 10~120 | 295 | 20 | - | - |
| HFe58-1-1 | R | >120~160 | - | - | - | - |
| HFe59-1-1 | R | 10~120 | 430 | 28 | 31 | - |
| HFe59-1-1 | R | >120~160 | - | - | - | - |
| HAl60-1 | R | 10~120 | 440 | 18 | - | - |
| HAl60-1 | R | >120~160 | - | - | - | - |
| HAl66-6-3-2 | R | 10~75 | >35 | 7 | - | - |
| HAl66-6-3-2 | R | >75~160 | - | - | - | -- |
| HAl67-2.5 | R | 10~75 | 395 | 15 | - | - |
| HAl67-2.5 | R | >75~160 | - | - | - | - |
| HAl77-2 | R | 10~75 | 245 | 40 | - | - |
| HAl77-2 | R | >75~160 | - | - | - | - |
| HNi56-3 | R | 10~75 | 440 | 25 | - | - |
| HNi56-3 | R | >75~160 | - | - | - | - |
| HSi80-3 | R | 10~75 | 295 | 25 | - | - |
| HSi80-3 | R | >75~160 | - | - | - | - |
| QAl19-2 | R | 10~45 | 490 | 15 | 18 | - |
| QAl19-2 | R | >45~120 | 470 | 20 | 24 | - |
| QAl19-2 | R | >120~160 | - | - | - | - |
| QAl9-4 | R | 10~120 | 540 | 15 | 17 | 110~190 |
| QAl9-4 | R | >120~160 | 450 | 12 | 13 | 110~190 |
| QAl10-3-1.5 | R | >10~16 | 610 | 8 | 9 | 130~190 |
| QAl10-3-1.5 | R | >15~160 | 590 | 12 | 13 | 130~190 |
| QAl10-4-4 | R | 10~29 | 690 | 4 | 5 | 17~240 |
| QAl10-4-4 | R | >29~120 | 635 | 5 | 6 | 170~240 |
| QAl10-4-4 | R | >120~160 | 590 | 5 | 6 | 170~240 |
| QAl11-6-6 | R | 10~28 | 690 | 4 | - | - |
| QAl11-6-6 | R | >28~50 | 635 | 5 | - | - |
| QAl11-6-6 | R | >50~160 | - | - | - | - |
| QSi1-3 | R | 20~80 | 490 | 10 | - | - |
| QSi1-3 | R | >80~100 | - | - | - | - |
| QSi3-1 | R | 20~100 | 345 | 20 | 23 | - |
| QSi3-1 | R | >100~160 | - | - | - | - |
| QSi3-1.5 | R | 40~120 | - | - | - | - |
| QSn4-3 | R | 40~120 | 275 | 25 | 30 | - |
| QSn6.5-0.1 | R | 30~40 | 355 | 50 | 55 | - |
| - | R | >40~100 | 345 | 55 | 60 | - |
| QSn6.5-0.4 | R | >100~120 | 305 | 58 | - | - |
| QSn7-0.2 | R | 40~120 | 355 | 55 | 64 | ≥70 |
| QC31 | R | 20~120 | 196 | 35 | - | ≤75 |
| QCr0.5 | R | 18~160 | - | - | - | - |
| BZn15-20 | R | 25~80 | 295 | 30 | - | - |
| BZn15-20 | R | >80~120 | - | - | - | - |
| BFe30-1-1 | R | 40~80 | 345 | 25 | - | - |
| BFe30-1-1 | R | >80~120 | - | - | - | - |
| BAl13-3 | R | 40~80 | 685 | 6 | - | - |
| BAl13-3 | R | >80~120 | - | - | - | - |
| BMn40-1.5 | R | 40~80 | 345 | 25 | - | - |
| BMn40-1.5 | R | >80~120 | - | - | - | - |
注：1.表中未規(guī)定力學(xué)性能指標(biāo)的產(chǎn)品，經(jīng)雙方協(xié)議，可供實(shí)測(cè)數(shù)據(jù)，但伸長(zhǎng)率供δ5。
2.伸長(zhǎng)率指標(biāo)若同時(shí)有δ10δ5，仲裁時(shí)以δ10為準(zhǔn)。
3.直徑小于16mm的棒材可不作布氏硬度試驗(yàn)。
4.直徑大于50mm的QAl10-3-1.5棒材，當(dāng)伸長(zhǎng)率δ10不小于15%時(shí)，其抗拉強(qiáng)度可不小于540MPa.
5.直徑10～120mm時(shí)的HFe59-1-1和HAl60-1-1棒材，當(dāng)σb和σ10數(shù)值之和不小于460時(shí)其伸長(zhǎng)率σ10分別可降至20%和15%
以上信息僅供參考